Backing is defined as material placed at the root of a weld joint for the purpose of supporting molten weld metal. Its function is to facilitate complete joint penetration.
Permanent backing is usually made from a base metal similar to that being welded and, as the name implies, becomes a permanent part of the joint because it is fused to the root of the weld and is not easy to remove.
Temporary backing may be made from copper or a ceramic substance that do not become fused to the root and are easily removed when welding is finished. This type of backing is also referred to as removable backing.
US terminology for a non-consumable material, either metallic or non-metallic, that is used to contain or shape the molten root run is a 'retainer'.
Welding the second side of a double-sided butt joint is regarded as welding a joint with backing because the first weld run put in from the second side is supported by weld metal from the first side.
For a single-sided, multi-process weld made without backing (open root) such as one with TIG root and MMA fill, the TIG root run is classed as a weld made without backing but the MMA fill is classed as a weld made with backing.
For welding procedure qualification, some welding codes classify the use of backing as an essential variable (EN 15614-1) but others classify it as non-essential (ASME Section IX).
For welder qualification, backing is invariably classed as an essential variable. This is because being able to produce a sound weld root using backing does not demonstrate he has skill required to make a sound weld without backing.
Pupose of backing material is of supporting molten weld metal and it's function is to facilitate complete joint penetration.
This helps welder to easily produce complete joint penetration by controlling the molten metal flow.
Material placed at the root of a weld joint for the purpose of supporting molten weld metal.
Its function is to facilitate complete joint penetration
for supporting molten weld metal and give CJP.
Material placed at the root of a weld joint for the purpose of supporting molten weld metal. Its function is to facilitate complete joint penetration.
TO SUPORTING MOLTING METAL..
To support the molten weld metal and to avoid from atmospheric contamination.
purpose of supporting molten weld metal protecting it from atmospheric contamination at the root and to facilitate complete joint penetration.