What weld defect often occurs weeks after welding the joint?

Question

muhammad rizwan ullah · Answer

DUE TO PRO CITY OR LACK OF FUSION

Ralph Bateman · Answer

The defect I was looking for is referenced as HIC (Hydrogen Induced Cracking)... a sneaky lil defect primarily caused by poor heat management, particularly when not managing the cooling rate properly. Results can be catastrophic!

ardel garcia · Answer

low amperage or no grinding

anilkumar yeshodharan · Answer

first rooted in the joint then weld joint

Anton Bester · Answer

When you not treed the welding spot with head treetment after it wash weld it will start to cold crac on that spot ofter weeks

Omar Uzcategui · Answer

Defect often occurs after welding is crack in Carbon Steels Cr-Mo (P3-P4 and P5 Numbers for Asme Code)

ROHITKUMAR RAKHOLIYA ROHIT · Answer

THE WELD DEFECT OFTENLY OCCURS IS COLD CRACK.

Mohamed Abdel Raheem Abdel Kader · Answer

hydrogen cracks

this problem can solved by using low Hydrogen electrods

Shaheen K M · Answer

Cold cracks..

IMRAN SHAIKH · Answer

<p>crack</p>

Products By Bayt.com

Use Our Mobile App

Start networking and exchanging professional insights

What weld defect often occurs weeks after welding the joint?

Popular Searches

More Questions Like This