What weld defect often occurs weeks after welding the joint?

Question

muhammad rizwan ullah · Answer

DUE TO PRO CITY OR LACK OF FUSION

Ralph Bateman · Answer

The defect I was looking for is referenced as HIC (Hydrogen Induced Cracking)... a sneaky lil defect primarily caused by poor heat management, particularly when not managing the cooling rate properly. Results can be catastrophic!

ardel garcia · Answer

low amperage or no grinding

anilkumar yeshodharan · Answer

first rooted in the joint then weld joint

Anton Bester · Answer

When you not treed the welding spot with head treetment after it wash weld it will start to cold crac on that spot ofter weeks

Omar Uzcategui · Answer

Defect often occurs after welding is crack in Carbon Steels Cr-Mo (P3-P4 and P5 Numbers for Asme Code)

ROHITKUMAR RAKHOLIYA ROHIT · Answer

THE WELD DEFECT OFTENLY OCCURS IS COLD CRACK.

Mohamed Abdel Raheem Abdel Kader · Answer

hydrogen cracks

this problem can solved by using low Hydrogen electrods

Shaheen K M · Answer

Cold cracks..

IMRAN SHAIKH · Answer

<p>crack</p>

Produits Par Bayt.com

Utilisez l'Appli de Bayt.com

Communiquez avec les autres et partagez vos connaissances professionnelles

What weld defect often occurs weeks after welding the joint?

Recherches Populaires

More Questions Like This